快干胶-1509L

Feature:Product 1509L is a high viscosity Ethyl-cyanoacrylate adhesive with superior peel and impact resistance. Suitable for bonding rubbers, metals and plastics. 
Material bonds:Plastic, rubber, metal. 
Typical applications:This product is good at no blooming requirement application and high temp requirement. And it also has good chemical resistant performance

分享

相关产品

 
 

Uncured properties

Property Value Test Method
Chemical nature modified ethyl cyanoacrylate  
Appearance colorless   
Viscosity 3000-6000 cps@20℃ 20rpm@25℃,ASTM D-1084
Flash point >87℃  
Specific Gravity 1.1 g/ml ASTM D-1875 
Gap filling 0.25mm   

 

Curing properties

Fixture time Value Test Method
PVC 15-70 s  
Phenolic Resin 10 - 30 s  
ABS 10 – 30 s   
Steel  15 – 45 s   
Aluminium 10 – 60 s  
Zinc bichromate  10 – 60 s  
Neoprene/NBR  10 - 30 s  
EPDM  30 -70 s   
Properties Value  Test Method
Tensile strength  16 - 26 N/mm² ASTM D 2095 
Shear strength  18 - 25 N/mm²  ISO 4587 
Impact strength  N.A  ASTM D 950 
Temperature range  -50 — 100℃  
Eelectrical Property Value Test Method
Electrical Resistivity >10E15 ohm.mm DIN 53482
Dielectric strength  25 KV/mm  ASTM D149 

 

Handling and Storage 
Apply Method:Dispense, brush 
Storage Method:8 - 21℃
Shelf life:6 months @ 20℃ 50% U.R 

 

Package available 
Bottle 20 gr – 500 gr 

 

Other Information 
The data contained herein are furnished for information only and are believed to be reliable. We cannot assume responsibility for the results obtained by others over whose methods we have no control. It is the user's responsibility to determine suitability for the user's purpose of any production methods mentioned herein and to adopt such precautions as may be advisable for the protection of property and of persons against any hazards that may be involved in the handling and use thereof. We recommend that each prospective user test his proposed application before repetitive use, using this data as a guide. The data may be updated without inform. 